Rotomolding Grade LLDPE Foaming Agent Material Compounding Powder

Product Description

Rotomolding Grade LLDPE Foaming Agent Material Compounding Powder, LLD484P is a foaming grade LLDPE modified rotoplastic powder with a foaming ratio of 4. The starting temperature is about 150℃, and the best foaming temperature is about 180℃.

Forms	● Commercial:active
Availability	● AS
Additive	● HS
Features
Uses	● Filling
Agency Ratings	● ROHS
Packaging	● 20Kg / packaging
Shelf Life	● 1 years from the date of production

Datasheet	Typical Values	Unit	Test Method
Physical
Density	-	g/cm3	ISO1183
Bulk Density	0.250	g/cm3	ISO60
Melt Index(190℃,2.16Kg)	3.2	g/10min	ISO1133
Dry Flow Rate	24	s/100g	ARM
E.S.C.R.	-	h	ASTM D1693
Melting Point	119	℃	ISO11357
Mechanical
Tensile Strength at Yield	6	MPa	ISO527
Tensile Elongation at Yield	50	%	ISO527
Flexural Modulus	210	MPa	ISO178
impact Strength	-	J/mm	ARM
Hardness, Shore D	-	D	ISO868
Thermal
Deflection Temperature(0.45MPa)	-	℃	ISO75
Vicat Softening Point	-	℃	ISO306
Brittleness Temperature	-	℃	ISO974
Aging
Oxidation Induction Time	20	min	ISO11357
UV Rating	-	h	ASTM 2565
Other
Surface Resistivity	-	Ω	IEC60093
Flame retardant	-	Grade	UL-94